Description of 6061 Aluminum Strip

Alloy: 6061
Temper: F,T6,T651,T9,T4,H111,H112
Mother coil: DC
Thickness: 0.8-6.0mm
Width: 800-2300mm
MOQ: 2-5 ton per size
Surface: clean and smooth,no bright speck,corrosion,oil,slotted,etc.
Package: export standard package,wooden pallet with fumigation
Delivery time: within 30days after receiving the deposit

Typical properties of Aluminium Strip 6061 

• Medium to high strength
• Good toughness
• Good surface finish
• Excellent corrosion resistance to atmospheric conditions
• Good corrosion resistance to sea water
• Can be anodized
• Good weldability and brazability
• Good workability
• Widely available

Features of 6061 Aluminium Strip

1.Moderate intensity
2.Rust-resistance
3.Good weld ability
4.Good oxidation effect
5.Easy polishing processing
6.Good plasticity
7.Easy to cold work ability
8.Easy to paint film

6061 Aluminium Strip Purpose

1.To make machine part,precision machining,aircraft parts,camera parts,coupler,hydraulic piston, brake piston,valve parts ,building pipeline,etc.
2. To make all kinds of industrial structure that required a certain strength and high corrosion resistance .
3.To make the truck,tower building,vessel,trolley,railway vehicle,furniture,etc.

Chemical Properties of 6061 Aluminium Strip

Alloy Designation		Si	Fe	Cu	Mn	Mg	Cr	Ni	Zn	Ti	Ga	V	Remarks	Others		Aluminium min
Numerical	Chemical Sympols													Each	Total
6061	AI Mg1SiCu	0.4-0.8	0.7	0.15-0.4	0.15	0.8-1.2	0.04- 0.35	-	0.25	0.15	-	-	-	0.05	0.15	Remainder

Alloy	Temper	Thickness(mm)	Width(mm)	Coil ID(mm)	Application
6061	O, T4, T6, T651	0.02~4.00	5~100	75, 150, 300, 400, 500	Cable,cosmetic cap, aluminum composite, pipe, aluminum hose or tube, electrical  transformer, shutter,aluminum battery

Typical Heat Treatment/Temper States

Treatment Definition F As fabricated 0 Annealed to obtain lower strength temper T1 Cooled from an elevated shaping process and naturally aged1 T4, T4511 Solution heat treated and naturally aged2,3 T51 Cooled from an elevated shaping process and artificially aged T6, T6511 Solution heat treated and artificially aged2,3